KB-TW(M) Magnetic heat shrink tube
Minimum fully recovery temperature: 110℃
Feature:
Shrink ratio : 2:1
Excellent EMC and EMI properties
Stable properties, easy installing, good shrink property
Application:
It is made of special irradiation cross-linked magnetic polyolefin compounds with good EMC and EMI properties to improve EMC properties of electronic appliances. It can be widely used in electronic appliance fields, i.e. inductance, capacitance, to alternate mutual-induction protector of electric induction coil to increase inductance and EMC. It is also used for electromagnetic shield in electronic circuits of PC power, capacitance and data wires.
|
Property |
Requirement |
Test method |
Typical data |
|
Longitudinal shrinkage |
≤10% |
ASTM D 2671 |
≤5% |
|
Tensile strength |
≥11.7MPa |
ASTM D 2671 |
≥12MPa |
|
Elongation at break |
≥300% |
ASTM D 2671 |
≥400% |
|
Dielectric voltage withstand |
1500V,60sec, no breakdown |
ASTM D 2671 |
No breakdown |
|
Volume resistivity |
≥1014Ω·cm |
ASTM D 876 |
≥1012Ω·cm |
|
Operating frequency |
|
|
1K～500KHz |
|
Inductance increase |
|
|
10% ～25% |
|
Size |
As supplied (mm) |
After recovered (mm) |
||
|
(min.)ID |
Wall thickness |
(max.)ID |
Wall thickness |
|
|
Ф3 |
3.5±0.3 |
0.25±0.05 |
1.5 |
0.45±0.10 |
|
Ф4 |
4.5±0.3 |
0.25±0.05 |
2.0 |
0.45±0.10 |
|
Ф4.5 |
5.0±0.3 |
0.25±0.05 |
2.3 |
0.50±0.10 |
|
Ф5 |
5.5±0.4 |
0.28±0.06 |
2.5 |
0.56±0.10 |
|
Ф6 |
6.5±0.4 |
0.28±0.06 |
3.0 |
0.56±0.10 |
|
Ф7 |
7.5±0.4 |
0.28±0.06 |
3.5 |
0.56±0.10 |
|
Ф8 |
8.5±0.4 |
0.28±0.06 |
4.0 |
0.60±0.10 |
|
Ф9 |
9.5±0.4 |
0.30±0.08 |
4.5 |
0.60±0.10 |
|
Ф10 |
10.5±0.4 |
0.30±0.08 |
5.0 |
0.60±0.10 |
|
Ф11 |
11.5±0.5 |
0.30±0.08 |
5.5 |
0.60±0.10 |
|
Ф12 |
12.5±0.5 |
0.30±0.08 |
6.0 |
0.60±0.10 |
|
Ф13 |
13.5±0.5 |
0.35±0.10 |
6.5 |
0.65±0.10 |
|
Ф14 |
14.5±0.5 |
0.35±0.10 |
7.0 |
0.65±0.10 |
|
Ф15 |
15.5±0.5 |
0.35±0.10 |
7.5 |
0.68±0.10 |
|
Other sizes are available upon request |
||||
|
Property |
Requirement |
Test method |
Typical data |
|
Longitudinal shrinkage |
≤10% |
ASTM D 2671 |
≤5% |
|
Tensile strength |
≥11.7MPa |
ASTM D 2671 |
≥12MPa |
|
Elongation at break |
≥300% |
ASTM D 2671 |
≥400% |
|
Dielectric voltage withstand |
1500V,60sec, no breakdown |
ASTM D 2671 |
No breakdown |
|
Volume resistivity |
≥1014Ω·cm |
ASTM D 876 |
≥1012Ω·cm |
|
Operating frequency |
|
|
1K～500KHz |
|
Inductance increase |
|
|
10% ～25% |
|
Size |
As supplied (mm) |
After recovered (mm) |
||
|
(min.)ID |
Wall thickness |
(max.)ID |
Wall thickness |
|
|
Ф3 |
3.5±0.3 |
0.25±0.05 |
1.5 |
0.45±0.10 |
|
Ф4 |
4.5±0.3 |
0.25±0.05 |
2.0 |
0.45±0.10 |
|
Ф4.5 |
5.0±0.3 |
0.25±0.05 |
2.3 |
0.50±0.10 |
|
Ф5 |
5.5±0.4 |
0.28±0.06 |
2.5 |
0.56±0.10 |
|
Ф6 |
6.5±0.4 |
0.28±0.06 |
3.0 |
0.56±0.10 |
|
Ф7 |
7.5±0.4 |
0.28±0.06 |
3.5 |
0.56±0.10 |
|
Ф8 |
8.5±0.4 |
0.28±0.06 |
4.0 |
0.60±0.10 |
|
Ф9 |
9.5±0.4 |
0.30±0.08 |
4.5 |
0.60±0.10 |
|
Ф10 |
10.5±0.4 |
0.30±0.08 |
5.0 |
0.60±0.10 |
|
Ф11 |
11.5±0.5 |
0.30±0.08 |
5.5 |
0.60±0.10 |
|
Ф12 |
12.5±0.5 |
0.30±0.08 |
6.0 |
0.60±0.10 |
|
Ф13 |
13.5±0.5 |
0.35±0.10 |
6.5 |
0.65±0.10 |
|
Ф14 |
14.5±0.5 |
0.35±0.10 |
7.0 |
0.65±0.10 |
|
Ф15 |
15.5±0.5 |
0.35±0.10 |
7.5 |
0.68±0.10 |
|
Other sizes are available upon request |
||||