Guangzhou Kebao insulation products Co., Ltd.
Русский
Special Shrink Tube
KB-SFS Shrinkable fabric sleeve
Temperature rating
� Operating temperature range (3000 hours): -40°C to 125°C
� Minimum recovery temperature: 100°C (recommended recovery temperature 110°C to 130°C)
� Maximum storage temperature: 60°C
Recovered after heating
� 2:1 shrink ratio
� Fully recoverable fabric wall thickness: Approximately 1 mm .
� Longitudinal change on full recovery is –10% to –20%.
|
Property |
Test condition(s) |
Performance* |
|
Abrasion resistance 200g load, 0.3mm radius metal blade, 10Hz, 10mm stroke, 144 000 cycles) |
23℃ |
No wear to underlying rubber hose |
|
80℃ |
No wear to underlying rubber hose |
|
|
125℃ |
No wear to underlying rubber hose |
|
|
Thermal ageing |
3000 hrs at 125°C |
No deterioration in abrasion resistance at80°C |
|
Low temperature flexibility |
4 hours at -40°C, 10X diameter mandrel |
No cracking |
|
Cold impact |
200g weight from 100mm at -40°C |
No cracking |
|
Thermal shock |
100 cycles between -40°C and 125°C |
No deterioration in abrasion resistance at 80°C |
|
Fluid resistance Antifreeze (50% ethylene glycol) Engine oil (SAE 10w/30) Mineral hydraulic fluid Detergent (1% Teepol) Brake fluid (DOT 4) Unleaded gasoline Diesel fuel Battery acid (1.25 SG H2SO4) |
24 hr immersion at 23°C |
No deterioration in abrasion resistance at 80°C |
| Size | Flat Width（mm) | ID as suplied（mm） | After shrinked（mm） |
| Φ6.0/3.0 | 12±2 | ≧6.0 | ≤3.0 |
| Φ8.0/4.0 | 16±2 | ≧8.0 | ≤4.0 |
| Φ10.0/5.0 | 20±2 | ≧10 | ≤5.0 |
| Φ12.0/6.0 | 24±3 | ≧12 | ≤6.0 |
| Φ14.0/7.0 | 27±3 | ≧14 | ≤7.0 |
| Φ16.0/8.0 | 29±3 | ≧16 | ≤8.0 |
| Φ20.0/10.0 | 36±3 | ≧20 | ≤10.0 |
| Φ25.0/12.5 | 44±3 | ≧25 | ≤12.5 |
| Φ30.0/15.0 | 53±4 | ≧30 | ≤15.0 |
| Φ35.0/17.5 | 60±4 | ≧35 | ≤17.5 |
| Φ40.0/20.0 | 68±4 | ≧40 | ≤20.0 |
| Φ45.0/22.5 | 76±4 | ≧45 | ≤22.5 |
| Φ50.0/25.0 | 85±5 | ≧50 | ≤25.0 |
| Φ60.0/30.0 | 100±5 | ≧60 | ≤30.0 |
| Φ65.0/32.5 | 107±5 | ≧65 | ≤32.5 |
| Φ70.0/35.0 | 116±5 | ≧70 | ≤35.0 |
| Φ80.0/40.0 | 132±5 | ≧80 | ≤40.0 |
| Φ90.0/45.0 | 145±5 | ≧90 | ≤45.0 |
|
Other sizes are available upon request. |
|||
|
Property |
Test condition(s) |
Performance* |
|
Abrasion resistance 200g load, 0.3mm radius metal blade, 10Hz, 10mm stroke, 144 000 cycles) |
23℃ |
No wear to underlying rubber hose |
|
80℃ |
No wear to underlying rubber hose |
|
|
125℃ |
No wear to underlying rubber hose |
|
|
Thermal ageing |
3000 hrs at 125°C |
No deterioration in abrasion resistance at80°C |
|
Low temperature flexibility |
4 hours at -40°C, 10X diameter mandrel |
No cracking |
|
Cold impact |
200g weight from 100mm at -40°C |
No cracking |
|
Thermal shock |
100 cycles between -40°C and 125°C |
No deterioration in abrasion resistance at 80°C |
|
Fluid resistance Antifreeze (50% ethylene glycol) Engine oil (SAE 10w/30) Mineral hydraulic fluid Detergent (1% Teepol) Brake fluid (DOT 4) Unleaded gasoline Diesel fuel Battery acid (1.25 SG H2SO4) |
24 hr immersion at 23°C |
No deterioration in abrasion resistance at 80°C |
| Size | Flat Width（mm) | ID as suplied（mm） | After shrinked（mm） |
| Φ6.0/3.0 | 12±2 | ≧6.0 | ≤3.0 |
| Φ8.0/4.0 | 16±2 | ≧8.0 | ≤4.0 |
| Φ10.0/5.0 | 20±2 | ≧10 | ≤5.0 |
| Φ12.0/6.0 | 24±3 | ≧12 | ≤6.0 |
| Φ14.0/7.0 | 27±3 | ≧14 | ≤7.0 |
| Φ16.0/8.0 | 29±3 | ≧16 | ≤8.0 |
| Φ20.0/10.0 | 36±3 | ≧20 | ≤10.0 |
| Φ25.0/12.5 | 44±3 | ≧25 | ≤12.5 |
| Φ30.0/15.0 | 53±4 | ≧30 | ≤15.0 |
| Φ35.0/17.5 | 60±4 | ≧35 | ≤17.5 |
| Φ40.0/20.0 | 68±4 | ≧40 | ≤20.0 |
| Φ45.0/22.5 | 76±4 | ≧45 | ≤22.5 |
| Φ50.0/25.0 | 85±5 | ≧50 | ≤25.0 |
| Φ60.0/30.0 | 100±5 | ≧60 | ≤30.0 |
| Φ65.0/32.5 | 107±5 | ≧65 | ≤32.5 |
| Φ70.0/35.0 | 116±5 | ≧70 | ≤35.0 |
| Φ80.0/40.0 | 132±5 | ≧80 | ≤40.0 |
| Φ90.0/45.0 | 145±5 | ≧90 | ≤45.0 |
|
Other sizes are available upon request. |
|||