Thin Wall Shrink Tube
KB-TW(P)Thin Wall Tube Rigid
Material: crosslinked modified semi-rigid polyolefin
Shrink ratio: 2: 1
Features:
• Excellent scratch resistance;
• At low temperatures good flexibility;
• meet automotive standards;
• excellent oil and chemical resistance;
• continuous use temperature: -35 ℃ ~ + 125 ℃
• Minimum shrink temperature: 110 ℃.
| Item
|
Specifications | |
| Shrink temperature (℃) | 120-150 | |
| Radial shrinkage (%) | ≥50 | |
| Longitudinal shrinkage(%) | ≤±5 | |
| Tensile strength (MPa) | ≥10.4 | |
| Elongation at break (%) | ≥200 | |
| Aging in circulating-air oven | 136.0±1.0℃, 168hrs | |
| After aging | Tensile strength (MPa) | ≥7.3 |
| Elongation at break (%) | ≥100 | |
| UL operation voltage (V) | 600 | |
| Volume resistivity (Ω·cm) | ≥1015 | |
| Dielectric strength (kV/mm) | ≥25 | |
| Concentricity (%) | ≥65 | |
Size
| Size | As supplied (mm) | After recovery (mm) | ||
| Inside diameter (D) | Wall thickness (T) | Inside diameter (d) | Wall thickness (t) | |
| Ф1.0 | 1.5+0.2/-0.1 | 0.18±0.05 | ≤0.60 | 0.36±0.08 |
| Ф1.5 | 2.1+0.2/-0.1 | 0.18±0.05 | ≤0.80 | 0.36±0.08 |
| Ф2.0 | 2.5+0.2/-0.1 | 0.20±0.05 | ≤1.00 | 0.42±0.08 |
| Ф2.5 | 3.0+0.2/-0.1 | 0.22±0.05 | ≤1.25 | 0.46±0.08 |
| Ф3.0 | 3.5+0.2/-0.1 | 0.22±0.05 | ≤1.50 | 0.46±0.08 |
| Ф3.5 | 4.0+0.2/-0.1 | 0.22±0.05 | ≤1.75 | 0.46±0.08 |
| Ф4.0 | 4.6+0.2/-0.1 | 0.22±0.05 | ≤2.00 | 0.46±0.08 |
| Ф4.5 | 5.0+0.2/-0.1 | 0.23±0.05 | ≤2.25 | 0.46±0.08 |
| Ф5.0 | 5.5+0.2/-0.1 | 0.25±0.05 | ≤2.50 | 0.50±0.08 |
| Ф6.0 | 6.5+0.2/-0.1 | 0.25±0.05 | ≤3.00 | 0.55±0.10 |
| Ф7.0 | 7.5+0.2/-0.1 | 0.25±0.05 | ≤3.50 | 0.55±0.10 |
| Ф8.0 | 8.5+0.3/-0.1 | 0.28±0.06 | ≤4.00 | 0.58±0.10 |
| Ф9.0 | 9.5+0.2/-0.1 | 0.28±0.06 | ≤4.50 | 0.58±0.10 |
| Ф10 | 10.5+0.3/-0.1 | 0.28±0.06 | ≤5.00 | 0.58±0.10 |
| Ф11 | 11.5+0.3/-0.1 | 0.28±0.06 | ≤5.50 | 0.58±0.10 |
| Ф12 | 12.5+0.3/-0.1 | 0.28±0.06 | ≤6.00 | 0.58±0.10 |
| Ф13 | 13.5+0.3/-0.1 | 0.28±0.06 | ≤6.50 | 0.58±0.10 |
| Ф14 | 14.5+0.3/-0.1 | 0.28±0.06 | ≤7.00 | 0.58±0.10 |
| Ф15 | 15.5+0.3/-0.1 | 0.28±0.06 | ≤7.50 | 0.58±0.10 |
| Ф16 | 16.5+0.3/-0.1 | 0.28±0.06 | ≤8.00 | 0.58±0.10 |
| Ф18 | 18.5+0.3/-0.1 | 0.32±0.08 | ≤9.00 | 0.68±0.10 |
| Ф20 | 20.6+0.5/-0.2 | 0.32±0.08 | ≤10.0 | 0.68±0.10 |
| Ф22 | 22.6+0.7/-0.2 | 0.35±0.08 | ≤11.0 | 0.72±0.12 |
| Ф25 | 25.6+0.7/-0.2 | 0.40±0.10 | ≤12.5 | 0.78±0.12 |
| Ф28 | 28.6+0.7/-0.2 | 0.40±0.10 | ≤14.0 | 0.78±0.12 |
| Ф30 | 30.6+0.7/-0.2 | 0.40±0.10 | ≤15.0 | 0.82±0.12 |
| Item
|
Specifications | |
| Shrink temperature (℃) | 120-150 | |
| Radial shrinkage (%) | ≥50 | |
| Longitudinal shrinkage(%) | ≤±5 | |
| Tensile strength (MPa) | ≥10.4 | |
| Elongation at break (%) | ≥200 | |
| Aging in circulating-air oven | 136.0±1.0℃, 168hrs | |
| After aging | Tensile strength (MPa) | ≥7.3 |
| Elongation at break (%) | ≥100 | |
| UL operation voltage (V) | 600 | |
| Volume resistivity (Ω·cm) | ≥1015 | |
| Dielectric strength (kV/mm) | ≥25 | |
| Concentricity (%) | ≥65 | |
Size
| Size | As supplied (mm) | After recovery (mm) | ||
| Inside diameter (D) | Wall thickness (T) | Inside diameter (d) | Wall thickness (t) | |
| Ф1.0 | 1.5+0.2/-0.1 | 0.18±0.05 | ≤0.60 | 0.36±0.08 |
| Ф1.5 | 2.1+0.2/-0.1 | 0.18±0.05 | ≤0.80 | 0.36±0.08 |
| Ф2.0 | 2.5+0.2/-0.1 | 0.20±0.05 | ≤1.00 | 0.42±0.08 |
| Ф2.5 | 3.0+0.2/-0.1 | 0.22±0.05 | ≤1.25 | 0.46±0.08 |
| Ф3.0 | 3.5+0.2/-0.1 | 0.22±0.05 | ≤1.50 | 0.46±0.08 |
| Ф3.5 | 4.0+0.2/-0.1 | 0.22±0.05 | ≤1.75 | 0.46±0.08 |
| Ф4.0 | 4.6+0.2/-0.1 | 0.22±0.05 | ≤2.00 | 0.46±0.08 |
| Ф4.5 | 5.0+0.2/-0.1 | 0.23±0.05 | ≤2.25 | 0.46±0.08 |
| Ф5.0 | 5.5+0.2/-0.1 | 0.25±0.05 | ≤2.50 | 0.50±0.08 |
| Ф6.0 | 6.5+0.2/-0.1 | 0.25±0.05 | ≤3.00 | 0.55±0.10 |
| Ф7.0 | 7.5+0.2/-0.1 | 0.25±0.05 | ≤3.50 | 0.55±0.10 |
| Ф8.0 | 8.5+0.3/-0.1 | 0.28±0.06 | ≤4.00 | 0.58±0.10 |
| Ф9.0 | 9.5+0.2/-0.1 | 0.28±0.06 | ≤4.50 | 0.58±0.10 |
| Ф10 | 10.5+0.3/-0.1 | 0.28±0.06 | ≤5.00 | 0.58±0.10 |
| Ф11 | 11.5+0.3/-0.1 | 0.28±0.06 | ≤5.50 | 0.58±0.10 |
| Ф12 | 12.5+0.3/-0.1 | 0.28±0.06 | ≤6.00 | 0.58±0.10 |
| Ф13 | 13.5+0.3/-0.1 | 0.28±0.06 | ≤6.50 | 0.58±0.10 |
| Ф14 | 14.5+0.3/-0.1 | 0.28±0.06 | ≤7.00 | 0.58±0.10 |
| Ф15 | 15.5+0.3/-0.1 | 0.28±0.06 | ≤7.50 | 0.58±0.10 |
| Ф16 | 16.5+0.3/-0.1 | 0.28±0.06 | ≤8.00 | 0.58±0.10 |
| Ф18 | 18.5+0.3/-0.1 | 0.32±0.08 | ≤9.00 | 0.68±0.10 |
| Ф20 | 20.6+0.5/-0.2 | 0.32±0.08 | ≤10.0 | 0.68±0.10 |
| Ф22 | 22.6+0.7/-0.2 | 0.35±0.08 | ≤11.0 | 0.72±0.12 |
| Ф25 | 25.6+0.7/-0.2 | 0.40±0.10 | ≤12.5 | 0.78±0.12 |
| Ф28 | 28.6+0.7/-0.2 | 0.40±0.10 | ≤14.0 | 0.78±0.12 |
| Ф30 | 30.6+0.7/-0.2 | 0.40±0.10 | ≤15.0 | 0.82±0.12 |