Identification Tube
KB-TWHF Halogen Free Heat Shrinkable Polyolefin Identification Sleeves
Next: KB-MTAG Tie on marker
| Item | Test method | Indicator |
| Tensile strength | SAE-AMS-DTL-23053 | ≥10.3MPa |
| Elongation at break | SAE-AMS-DTL-23053 | ≥200% |
| Low temperature flexibility | SAE-AMS-DTL-23053.4.6.7 | -55℃±1℃，4h,No cracks |
| Hot Shock | SAE-AMS-DTL-23053.4.6.8 | 250℃±3℃，4h,No cracks, No dripping, No flow |
| Aging properties | SAE-AMS-DTL-23053.4.6.9 | 175℃±2℃，168h No damage (visually intuitive damage) |
| Tensile strength after aging | SAE-AMS-DTL-23053.4.6.13AndASTM D638 | ≥6.9MPa，23℃±2℃ |
| Elongation at break after aging | SAE-AMS-DTL-23053.4.6.13和ASTM D638 | ≥100%，23℃±2℃ |
| Color stability | SAE-AMS-DTL-23053.4.6.15 | 175℃±2℃,24h,by |
| Dielectric strength | SAE-AMS-DTL-23053.4.6.13AndASTM D2671 | ≥19.7kV/mm,23℃±2℃ |
| Volume resistivity | SAE-AMS-DTL-23053.4.6.13AndASTM D876 | ≥1.0x1014Ω· cm,500V（DC）,60s |
| Flame retardant | SAE-AMS-DTL-23053.4.6.14 ASTM D2671 UL224 | Self-extinguishing within 60s, more than 25% of the iconic flag is damaged or burned, no dripping and a large area falling |
| Antibody solution performance | AE-AMS-DTL-23053.4.6.11 | No damage (visually intuitive damage) |
| Printing durability | SAE-AS-81531.4.6.2 | Eraser 50 times, the writing is clearly visible |
| Printing solvent resistance | MIL-STD-202G Method 215K | Eraser 10 times, the writing is clearly visible |
| Specification | Dimension before shrinkage（mm） | Dimension before shrinkage（mm） | Continuous packing (m/plate) | Quantity per reel cassette packaging | ||
| Diameter（D） | Thickness（T） | Diameter（d） | Thickness（t） | |||
| Ф2.4(2X) | ≥2.4 | 0.27±0.05 | ≤1.2 | 0.51±0.08 | 30 | 2000 |
| Ф3.2(2X) | ≥3.2 | 0.27±0.05 | ≤1.6 | 0.51±0.08 | 30 | 2000 |
| Ф4.8(2X) | ≥4.8 | 0.27±0.05 | ≤2.4 | 0.51±0.08 | 30 | 2000 |
| Ф6.4(2X) | ≥6.4 | 0.32±0.06 | ≤3.2 | 0.64±0.08 | 30 | 1500 |
| Ф9.5(2X) | ≥9.5 | 0.32±0.06 | ≤4.8 | 0.64±0.08 | 30 | 1500 |
| Ф12.7(2X) | ≥12.7 | 0.32±0.06 | ≤6.4 | 0.64±0.08 | 30 | 500 |
| Ф19.1(2X) | ≥19.1 | 0.36±0.06 | ≤9.5 | 0.76±0.08 | 30 | 500 |
| Ф25.4(2X) | ≥25.4 | 0.45±0.08 | ≤12.7 | 0.89±0.08 | 30 | 250 |
| Ф38.1(2X) | ≥38.1 | 0.50±0.08 | ≤19.1 | 1.02±0.15 | 30 | 250 |
| Ф50.8(2X) | ≥50.8 | 0.58±0.08 | ≤25.4 | 1.14±0.18 | 30 | 250 |
| Shrink Ratio:3:1 | ||||||
| Ф2.4(3X) | ≥2.4 | 0.22±0.05 | ≤0.8 | 0.53±0.08 | 30 | 2000 |
| Ф3.2(3X) | ≥3.2 | 0.22±0.05 | ≤1.1 | 0.58±0.08 | 30 | 2000 |
| Ф4.8(3X) | ≥4.8 | 0.22±0.05 | ≤1.6 | 0.58±0.08 | 30 | 2000 |
| Ф6.4(3X) | ≥6.4 | 0.22±0.05 | ≤2.1 | 0.58±0.08 | 30 | 1500 |
| Ф9.5(3X) | ≥9.5 | 0.20±0.05 | ≤3.2 | 0.61±0.08 | 30 | 1500 |
| Ф12.7(3X) | ≥12.7 | 0.20±0.05 | ≤4.2 | 0.61±0.08 | 30 | 500 |
| Ф19.1(3X) | ≥19.1 | 0.20±0.05 | ≤6.4 | 0.61±0.08 | 30 | 500 |
| Ф25.4(3X) | ≥25.4 | 0.20±0.05 | ≤8.5 | 0.64±0.08 | 30 | 250 |
| Ф38.1(3X) | ≥38.1 | 0.30±0.06 | ≤12.7 | 1.00±0.15 | 30 | 250 |
| Ф50.8(3X) | ≥50.8 | 0.30±0.06 | ≤17.0 | 1.00±0.18 | 30 | 250 |
| Item | Test method | Indicator |
| Tensile strength | SAE-AMS-DTL-23053 | ≥10.3MPa |
| Elongation at break | SAE-AMS-DTL-23053 | ≥200% |
| Low temperature flexibility | SAE-AMS-DTL-23053.4.6.7 | -55℃±1℃，4h,No cracks |
| Hot Shock | SAE-AMS-DTL-23053.4.6.8 | 250℃±3℃，4h,No cracks, No dripping, No flow |
| Aging properties | SAE-AMS-DTL-23053.4.6.9 | 175℃±2℃，168h No damage (visually intuitive damage) |
| Tensile strength after aging | SAE-AMS-DTL-23053.4.6.13AndASTM D638 | ≥6.9MPa，23℃±2℃ |
| Elongation at break after aging | SAE-AMS-DTL-23053.4.6.13和ASTM D638 | ≥100%，23℃±2℃ |
| Color stability | SAE-AMS-DTL-23053.4.6.15 | 175℃±2℃,24h,by |
| Dielectric strength | SAE-AMS-DTL-23053.4.6.13AndASTM D2671 | ≥19.7kV/mm,23℃±2℃ |
| Volume resistivity | SAE-AMS-DTL-23053.4.6.13AndASTM D876 | ≥1.0x1014Ω· cm,500V（DC）,60s |
| Flame retardant | SAE-AMS-DTL-23053.4.6.14 ASTM D2671 UL224 | Self-extinguishing within 60s, more than 25% of the iconic flag is damaged or burned, no dripping and a large area falling |
| Antibody solution performance | AE-AMS-DTL-23053.4.6.11 | No damage (visually intuitive damage) |
| Printing durability | SAE-AS-81531.4.6.2 | Eraser 50 times, the writing is clearly visible |
| Printing solvent resistance | MIL-STD-202G Method 215K | Eraser 10 times, the writing is clearly visible |
| Specification | Dimension before shrinkage（mm） | Dimension before shrinkage（mm） | Continuous packing (m/plate) | Quantity per reel cassette packaging | ||
| Diameter（D） | Thickness（T） | Diameter（d） | Thickness（t） | |||
| Ф2.4(2X) | ≥2.4 | 0.27±0.05 | ≤1.2 | 0.51±0.08 | 30 | 2000 |
| Ф3.2(2X) | ≥3.2 | 0.27±0.05 | ≤1.6 | 0.51±0.08 | 30 | 2000 |
| Ф4.8(2X) | ≥4.8 | 0.27±0.05 | ≤2.4 | 0.51±0.08 | 30 | 2000 |
| Ф6.4(2X) | ≥6.4 | 0.32±0.06 | ≤3.2 | 0.64±0.08 | 30 | 1500 |
| Ф9.5(2X) | ≥9.5 | 0.32±0.06 | ≤4.8 | 0.64±0.08 | 30 | 1500 |
| Ф12.7(2X) | ≥12.7 | 0.32±0.06 | ≤6.4 | 0.64±0.08 | 30 | 500 |
| Ф19.1(2X) | ≥19.1 | 0.36±0.06 | ≤9.5 | 0.76±0.08 | 30 | 500 |
| Ф25.4(2X) | ≥25.4 | 0.45±0.08 | ≤12.7 | 0.89±0.08 | 30 | 250 |
| Ф38.1(2X) | ≥38.1 | 0.50±0.08 | ≤19.1 | 1.02±0.15 | 30 | 250 |
| Ф50.8(2X) | ≥50.8 | 0.58±0.08 | ≤25.4 | 1.14±0.18 | 30 | 250 |
| Shrink Ratio:3:1 | ||||||
| Ф2.4(3X) | ≥2.4 | 0.22±0.05 | ≤0.8 | 0.53±0.08 | 30 | 2000 |
| Ф3.2(3X) | ≥3.2 | 0.22±0.05 | ≤1.1 | 0.58±0.08 | 30 | 2000 |
| Ф4.8(3X) | ≥4.8 | 0.22±0.05 | ≤1.6 | 0.58±0.08 | 30 | 2000 |
| Ф6.4(3X) | ≥6.4 | 0.22±0.05 | ≤2.1 | 0.58±0.08 | 30 | 1500 |
| Ф9.5(3X) | ≥9.5 | 0.20±0.05 | ≤3.2 | 0.61±0.08 | 30 | 1500 |
| Ф12.7(3X) | ≥12.7 | 0.20±0.05 | ≤4.2 | 0.61±0.08 | 30 | 500 |
| Ф19.1(3X) | ≥19.1 | 0.20±0.05 | ≤6.4 | 0.61±0.08 | 30 | 500 |
| Ф25.4(3X) | ≥25.4 | 0.20±0.05 | ≤8.5 | 0.64±0.08 | 30 | 250 |
| Ф38.1(3X) | ≥38.1 | 0.30±0.06 | ≤12.7 | 1.00±0.15 | 30 | 250 |
| Ф50.8(3X) | ≥50.8 | 0.30±0.06 | ≤17.0 | 1.00±0.18 | 30 | 250 |