Guangzhou Kebao insulation products Co., Ltd.
Русский
Identification Tube
MTHF Halogen Free Heat Shrinkable Polyolefin Identification Sleeves
Previous: KB-MTAG Tie on marker
|
Item |
Test method |
Indicator |
|
Tensile strength |
SAE-AMS-DTL-23053 |
≥10.3MPa |
|
Elongation at break |
SAE-AMS-DTL-23053 |
≥200% |
|
Low temperature flexibility |
SAE-AMS-DTL-23053.4.6.7 |
-55℃±1℃，4h,No cracks |
|
Hot Shock |
SAE-AMS-DTL-23053.4.6.8 |
250℃±3℃，4h,No cracks, No dripping, No flow |
|
Aging properties |
SAE-AMS-DTL-23053.4.6.9 |
175℃±2℃，168h No damage (visually intuitive damage) |
|
Tensile strength after aging |
SAE-AMS-DTL-23053.4.6.13AndASTM D638 |
≥6.9MPa，23℃±2℃ |
|
Elongation at break after aging |
SAE-AMS-DTL-23053.4.6.13和ASTM D638 |
≥100%，23℃±2℃ |
|
Color stability |
SAE-AMS-DTL-23053.4.6.15 |
175℃±2℃,24h,by |
|
Dielectric strength |
SAE-AMS-DTL-23053.4.6.13AndASTM D2671 |
≥19.7kV/mm,23℃±2℃ |
|
Volume resistivity |
SAE-AMS-DTL-23053.4.6.13AndASTM D876 |
≥1.0x1014Ω· cm,500V（DC）,60s |
|
Flame retardant |
SAE-AMS-DTL-23053.4.6.14 ASTM D2671 UL224 |
Self-extinguishing within 60s, more than 25% of the iconic flag is damaged or burned, no dripping and a large area falling |
|
Antibody solution performance |
AE-AMS-DTL-23053.4.6.11 |
No damage (visually intuitive damage) |
|
Printing durability |
SAE-AS-81531.4.6.2 |
Eraser 50 times, the writing is clearly visible |
|
Printing solvent resistance |
MIL-STD-202G Method 215K |
Eraser 10 times, the writing is clearly visible |
|
Specification |
Dimension before shrinkage（mm） |
Dimension before shrinkage（mm） |
Continuous packing (m/plate) |
Quantity per reel cassette packaging |
||
|
Diameter（D） |
Thickness（T） |
Diameter（d） |
Thickness（t） |
|||
|
Ф2.4(2X) |
≥2.4 |
0.27±0.05 |
≤1.2 |
0.51±0.08 |
30 |
2000 |
|
Ф3.2(2X) |
≥3.2 |
0.27±0.05 |
≤1.6 |
0.51±0.08 |
30 |
2000 |
|
Ф4.8(2X) |
≥4.8 |
0.27±0.05 |
≤2.4 |
0.51±0.08 |
30 |
2000 |
|
Ф6.4(2X) |
≥6.4 |
0.32±0.06 |
≤3.2 |
0.64±0.08 |
30 |
1500 |
|
Ф9.5(2X) |
≥9.5 |
0.32±0.06 |
≤4.8 |
0.64±0.08 |
30 |
1500 |
|
Ф12.7(2X) |
≥12.7 |
0.32±0.06 |
≤6.4 |
0.64±0.08 |
30 |
500 |
|
Ф19.1(2X) |
≥19.1 |
0.36±0.06 |
≤9.5 |
0.76±0.08 |
30 |
500 |
|
Ф25.4(2X) |
≥25.4 |
0.45±0.08 |
≤12.7 |
0.89±0.08 |
30 |
250 |
|
Ф38.1(2X) |
≥38.1 |
0.50±0.08 |
≤19.1 |
1.02±0.15 |
30 |
250 |
|
Ф50.8(2X) |
≥50.8 |
0.58±0.08 |
≤25.4 |
1.14±0.18 |
30 |
250 |
|
Shrink Ratio:3:1 |
||||||
|
Ф2.4(3X) |
≥2.4 |
0.22±0.05 |
≤0.8 |
0.53±0.08 |
30 |
2000 |
|
Ф3.2(3X) |
≥3.2 |
0.22±0.05 |
≤1.1 |
0.58±0.08 |
30 |
2000 |
|
Ф4.8(3X) |
≥4.8 |
0.22±0.05 |
≤1.6 |
0.58±0.08 |
30 |
2000 |
|
Ф6.4(3X) |
≥6.4 |
0.22±0.05 |
≤2.1 |
0.58±0.08 |
30 |
1500 |
|
Ф9.5(3X) |
≥9.5 |
0.20±0.05 |
≤3.2 |
0.61±0.08 |
30 |
1500 |
|
Ф12.7(3X) |
≥12.7 |
0.20±0.05 |
≤4.2 |
0.61±0.08 |
30 |
500 |
|
Ф19.1(3X) |
≥19.1 |
0.20±0.05 |
≤6.4 |
0.61±0.08 |
30 |
500 |
|
Ф25.4(3X) |
≥25.4 |
0.20±0.05 |
≤8.5 |
0.64±0.08 |
30 |
250 |
|
Ф38.1(3X) |
≥38.1 |
0.30±0.06 |
≤12.7 |
1.00±0.15 |
30 |
250 |
|
Ф50.8(3X) |
≥50.8 |
0.30±0.06 |
≤17.0 |
1.00±0.18 |
30 |
250 |
Other sizes are available upon request.
|
Item |
Test method |
Indicator |
|
Tensile strength |
SAE-AMS-DTL-23053 |
≥10.3MPa |
|
Elongation at break |
SAE-AMS-DTL-23053 |
≥200% |
|
Low temperature flexibility |
SAE-AMS-DTL-23053.4.6.7 |
-55℃±1℃，4h,No cracks |
|
Hot Shock |
SAE-AMS-DTL-23053.4.6.8 |
250℃±3℃，4h,No cracks, No dripping, No flow |
|
Aging properties |
SAE-AMS-DTL-23053.4.6.9 |
175℃±2℃，168h No damage (visually intuitive damage) |
|
Tensile strength after aging |
SAE-AMS-DTL-23053.4.6.13AndASTM D638 |
≥6.9MPa，23℃±2℃ |
|
Elongation at break after aging |
SAE-AMS-DTL-23053.4.6.13和ASTM D638 |
≥100%，23℃±2℃ |
|
Color stability |
SAE-AMS-DTL-23053.4.6.15 |
175℃±2℃,24h,by |
|
Dielectric strength |
SAE-AMS-DTL-23053.4.6.13AndASTM D2671 |
≥19.7kV/mm,23℃±2℃ |
|
Volume resistivity |
SAE-AMS-DTL-23053.4.6.13AndASTM D876 |
≥1.0x1014Ω· cm,500V（DC）,60s |
|
Flame retardant |
SAE-AMS-DTL-23053.4.6.14 ASTM D2671 UL224 |
Self-extinguishing within 60s, more than 25% of the iconic flag is damaged or burned, no dripping and a large area falling |
|
Antibody solution performance |
AE-AMS-DTL-23053.4.6.11 |
No damage (visually intuitive damage) |
|
Printing durability |
SAE-AS-81531.4.6.2 |
Eraser 50 times, the writing is clearly visible |
|
Printing solvent resistance |
MIL-STD-202G Method 215K |
Eraser 10 times, the writing is clearly visible |
|
Specification |
Dimension before shrinkage（mm） |
Dimension before shrinkage（mm） |
Continuous packing (m/plate) |
Quantity per reel cassette packaging |
||
|
Diameter（D） |
Thickness（T） |
Diameter（d） |
Thickness（t） |
|||
|
Ф2.4(2X) |
≥2.4 |
0.27±0.05 |
≤1.2 |
0.51±0.08 |
30 |
2000 |
|
Ф3.2(2X) |
≥3.2 |
0.27±0.05 |
≤1.6 |
0.51±0.08 |
30 |
2000 |
|
Ф4.8(2X) |
≥4.8 |
0.27±0.05 |
≤2.4 |
0.51±0.08 |
30 |
2000 |
|
Ф6.4(2X) |
≥6.4 |
0.32±0.06 |
≤3.2 |
0.64±0.08 |
30 |
1500 |
|
Ф9.5(2X) |
≥9.5 |
0.32±0.06 |
≤4.8 |
0.64±0.08 |
30 |
1500 |
|
Ф12.7(2X) |
≥12.7 |
0.32±0.06 |
≤6.4 |
0.64±0.08 |
30 |
500 |
|
Ф19.1(2X) |
≥19.1 |
0.36±0.06 |
≤9.5 |
0.76±0.08 |
30 |
500 |
|
Ф25.4(2X) |
≥25.4 |
0.45±0.08 |
≤12.7 |
0.89±0.08 |
30 |
250 |
|
Ф38.1(2X) |
≥38.1 |
0.50±0.08 |
≤19.1 |
1.02±0.15 |
30 |
250 |
|
Ф50.8(2X) |
≥50.8 |
0.58±0.08 |
≤25.4 |
1.14±0.18 |
30 |
250 |
|
Shrink Ratio:3:1 |
||||||
|
Ф2.4(3X) |
≥2.4 |
0.22±0.05 |
≤0.8 |
0.53±0.08 |
30 |
2000 |
|
Ф3.2(3X) |
≥3.2 |
0.22±0.05 |
≤1.1 |
0.58±0.08 |
30 |
2000 |
|
Ф4.8(3X) |
≥4.8 |
0.22±0.05 |
≤1.6 |
0.58±0.08 |
30 |
2000 |
|
Ф6.4(3X) |
≥6.4 |
0.22±0.05 |
≤2.1 |
0.58±0.08 |
30 |
1500 |
|
Ф9.5(3X) |
≥9.5 |
0.20±0.05 |
≤3.2 |
0.61±0.08 |
30 |
1500 |
|
Ф12.7(3X) |
≥12.7 |
0.20±0.05 |
≤4.2 |
0.61±0.08 |
30 |
500 |
|
Ф19.1(3X) |
≥19.1 |
0.20±0.05 |
≤6.4 |
0.61±0.08 |
30 |
500 |
|
Ф25.4(3X) |
≥25.4 |
0.20±0.05 |
≤8.5 |
0.64±0.08 |
30 |
250 |
|
Ф38.1(3X) |
≥38.1 |
0.30±0.06 |
≤12.7 |
1.00±0.15 |
30 |
250 |
|
Ф50.8(3X) |
≥50.8 |
0.30±0.06 |
≤17.0 |
1.00±0.18 |
30 |
250 |
Other sizes are available upon request.
Give Us A Message