Guangzhou Kebao insulation products Co., Ltd.
Русский
Special Shrink Tube
KB-SFS Shrinkable fabric sleeve
|
Property |
Test condition(s) |
Performance* |
|
Abrasion resistance 200g load, 0.3mm radius metal blade, 10Hz, 10mm stroke, 144 000 cycles) |
23℃ |
No wear to underlying rubber hose |
|
80℃ |
No wear to underlying rubber hose |
|
|
125℃ |
No wear to underlying rubber hose |
|
|
Thermal ageing |
3000 hrs at 125°C |
No deterioration in abrasion resistance at80°C |
|
Low temperature flexibility |
4 hours at -40°C, 10X diameter mandrel |
No cracking |
|
Cold impact |
200g weight from 100mm at -40°C |
No cracking |
|
Thermal shock |
100 cycles between -40°C and 125°C |
No deterioration in abrasion resistance at 80°C |
|
Fluid resistance Antifreeze (50% ethylene glycol) Engine oil (SAE 10w/30) Mineral hydraulic fluid Detergent (1% Teepol) Brake fluid (DOT 4) Unleaded gasoline Diesel fuel Battery acid (1.25 SG H2SO4) |
24 hr immersion at 23°C |
No deterioration in abrasion resistance at 80°C |
|
Size |
Flat Width（mm) |
ID as suplied（mm） |
After shrinked（mm） |
|
Φ6.0/3.0 |
12±2 |
≧6.0 |
≤3.0 |
|
Φ8.0/4.0 |
16±2 |
≧8.0 |
≤4.0 |
|
Φ10.0/5.0 |
20±2 |
≧10 |
≤5.0 |
|
Φ12.0/6.0 |
24±3 |
≧12 |
≤6.0 |
|
Φ14.0/7.0 |
27±3 |
≧14 |
≤7.0 |
|
Φ16.0/8.0 |
29±3 |
≧16 |
≤8.0 |
|
Φ20.0/10.0 |
36±3 |
≧20 |
≤10.0 |
|
Φ25.0/12.5 |
44±3 |
≧25 |
≤12.5 |
|
Φ30.0/15.0 |
53±4 |
≧30 |
≤15.0 |
|
Φ35.0/17.5 |
60±4 |
≧35 |
≤17.5 |
|
Φ40.0/20.0 |
68±4 |
≧40 |
≤20.0 |
|
Φ45.0/22.5 |
76±4 |
≧45 |
≤22.5 |
|
Φ50.0/25.0 |
85±5 |
≧50 |
≤25.0 |
|
Φ60.0/30.0 |
100±5 |
≧60 |
≤30.0 |
|
Φ65.0/32.5 |
107±5 |
≧65 |
≤32.5 |
|
Φ70.0/35.0 |
116±5 |
≧70 |
≤35.0 |
|
Φ80.0/40.0 |
132±5 |
≧80 |
≤40.0 |
|
Φ90.0/45.0 |
145±5 |
≧90 |
≤45.0 |
|
Other sizes are available upon request. |
|||
|
Property |
Test condition(s) |
Performance* |
|
Abrasion resistance 200g load, 0.3mm radius metal blade, 10Hz, 10mm stroke, 144 000 cycles) |
23℃ |
No wear to underlying rubber hose |
|
80℃ |
No wear to underlying rubber hose |
|
|
125℃ |
No wear to underlying rubber hose |
|
|
Thermal ageing |
3000 hrs at 125°C |
No deterioration in abrasion resistance at80°C |
|
Low temperature flexibility |
4 hours at -40°C, 10X diameter mandrel |
No cracking |
|
Cold impact |
200g weight from 100mm at -40°C |
No cracking |
|
Thermal shock |
100 cycles between -40°C and 125°C |
No deterioration in abrasion resistance at 80°C |
|
Fluid resistance Antifreeze (50% ethylene glycol) Engine oil (SAE 10w/30) Mineral hydraulic fluid Detergent (1% Teepol) Brake fluid (DOT 4) Unleaded gasoline Diesel fuel Battery acid (1.25 SG H2SO4) |
24 hr immersion at 23°C |
No deterioration in abrasion resistance at 80°C |
|
Size |
Flat Width（mm) |
ID as suplied（mm） |
After shrinked（mm） |
|
Φ6.0/3.0 |
12±2 |
≧6.0 |
≤3.0 |
|
Φ8.0/4.0 |
16±2 |
≧8.0 |
≤4.0 |
|
Φ10.0/5.0 |
20±2 |
≧10 |
≤5.0 |
|
Φ12.0/6.0 |
24±3 |
≧12 |
≤6.0 |
|
Φ14.0/7.0 |
27±3 |
≧14 |
≤7.0 |
|
Φ16.0/8.0 |
29±3 |
≧16 |
≤8.0 |
|
Φ20.0/10.0 |
36±3 |
≧20 |
≤10.0 |
|
Φ25.0/12.5 |
44±3 |
≧25 |
≤12.5 |
|
Φ30.0/15.0 |
53±4 |
≧30 |
≤15.0 |
|
Φ35.0/17.5 |
60±4 |
≧35 |
≤17.5 |
|
Φ40.0/20.0 |
68±4 |
≧40 |
≤20.0 |
|
Φ45.0/22.5 |
76±4 |
≧45 |
≤22.5 |
|
Φ50.0/25.0 |
85±5 |
≧50 |
≤25.0 |
|
Φ60.0/30.0 |
100±5 |
≧60 |
≤30.0 |
|
Φ65.0/32.5 |
107±5 |
≧65 |
≤32.5 |
|
Φ70.0/35.0 |
116±5 |
≧70 |
≤35.0 |
|
Φ80.0/40.0 |
132±5 |
≧80 |
≤40.0 |
|
Φ90.0/45.0 |
145±5 |
≧90 |
≤45.0 |
|
Other sizes are available upon request. |
|||